Standard : ASTM A588 / ASME SA588
Grade : ASTM A588 Gr A Corten Steel Plates
Standard : ASTM A588 / ASME SA588
Width : from 750mm to 1500mm
Length : upto 12,000mm
Thickness : from 0.8 mm to 50mm
Type : Corten Steel
Process : Hot-Rolled (HR)
ASTM A588 Grade A Corten Steel Plates Chemical Composition
| Grade | C % | Si % | Mn % | P % | S % | Cr % | V % | Ni % | Cu % |
| A588 Gr A | 0.19 | 0.30-0.65 | 0.80-1.25 | 0.04 | 0.05 | 0.40-0.65 | 0.02-0.10 | 0.40 | 0.25-0.5 |
| A588 Gr B | ≤0.20 | 0.15-0.50 | 0.75-1.35 | 0.040 | 0.050 | 0.40-0.70 | 0.01-0.10 | ≤0.50 | ≤0.50 |
ASTM A588 Gr A Corten Steel Plates Mechanical Propertiesption
| Grade | Thickness | Yield Strength ReH[N/mm2]transv.min |
TensileStrength Rm[N/mm2]transv |
| ASTM A588 | 0mm-100mm | 340 MPa | 480 MPa |
| 102mm-127mm | 320 MPa | 460 MPa | |
| 127mm-203mm | 290 MPa | 430 MPa |
The weathering resistance of ASTM A588 grade A weathering steel in construction also slows down the corrosion phenomenon of buildings, and achieves a good application effect.
Welding weathering steel is relatively simple. It is very similar to some of the common low carbon steels such as ASTM A588 weathering steel is a structural steel covered under the AWS D1.1. Structural Welding Code. It is a group II steel which means prequalified welding procedures may be used.
Process of ASTM A588 Gr.A weathering steel and stainless steel plates respectively
After polishing and removing the dirt around the groove, pair the groove of ASTM A588 Gr.A weathering steel with the groove of the stainless steel plate to form a welding area;
Non-pulsating solder is used in the weld zone formed between ASTM A588 Gr.A weathering steel and the stainless steel plate to form a primer layer at the lower part of the weld zone;
Non-pulsating solder is used to cover the upper surface of the soldering layer in the soldering zone to form a covering layer in the ASTM A588 Gr.A weathering steel soldering area. By welding weather-resistant plates and stainless steel plates under low current and voltage, reducing the heat of
ASTM A588 Gr.A weathering steel and stainless steel during the welding process, effectively reducing the melting rate of the two plates, and manufacturing ASTM A588 Gr.A weathering steel and stainless steel. It can be more completely fused to improve the weldability of welding.