Beams Wide Flange (W) W18x65

W18x65 h profile steel Specifications
The section height is 18.4 inches (about 467mm).
The section width is 7.59 inches (about 193mm).
The flange thickness is 0.75 inches (about 19.1mm).
The web thickness is 0.45 inches (about 11.4mm).
The fillet radius is 0.4 inches.
The cross-sectional area is 19.1 square inches (about 12323 square millimeters).
Weight: 65 pounds per foot, which is about 97kg per meter after conversion.

W18x65 h beam structure Mechanical properties
Bending capacity: The cross-sectional shape is reasonable, and it has strong bending capacity in all directions. It can withstand large moment loads. It is suitable for use as structural components such as beams and columns. It can effectively support the weight of the structure and withstand external forces in construction, bridges and other projects.

Yield strength: If the material is A36, the yield strength is about 250MPa; if it is A572GR50, the yield strength is 345MPa; if it is A992, the yield strength is usually not less than 345MPa. The specific value may vary slightly depending on the manufacturer and production process.

W18x65 h shaped beam Application field
Construction field: It is widely used in the steel structure frame of industrial and civil buildings, such as factories, high-rise buildings, etc. It can be used as beam and column components, which can effectively improve the bearing capacity and spatial performance of the structure. At the same time, due to its simple construction, it can shorten the construction period.

Bridge engineering: It can be used to build the upper and lower structures of bridges, such as piers, abutments and bridge decks, etc., and can withstand various loads borne by bridges, including vehicle loads, wind loads and earthquake loads.

Machinery manufacturing: In the manufacture of mining machinery, metallurgical machinery, ship machinery and other equipment, it can be used to manufacture the skeleton structure of equipment to withstand various forces and torques during the operation of the equipment.

GNEE production process
We usually use hot rolling process to produce, by heating the steel billet and rolling it on the rolling mill to form a specific H-shaped steel section shape. The hot rolling process can make the steel obtain good mechanical properties and surface quality.