What is grade of P275N Pressure Vessel Steel Plate

P275N pressure vessels steel plate is a normalized fine-grained structural steel grade defined under the EN 10028-3. It is specifically designed for use in pressure vessels, boilers, and heat-resistant equipment, where reliable strength and weldability are required.

P275N pressure vessels steel plate

The designation P275N follows a standard naming convention:

P = Pressure vessel steel

275 = Minimum yield strength of 275 MPa

N = Normalized or normalized rolled delivery condition

So, P275N Material is a normalized pressure vessel steel grade with a minimum yield strength of 275 MPa.

This classification ensures that P275N pressure vessels steel meets strict requirements for mechanical properties and weldability.

These properties make P275N Material suitable for medium-pressure and moderate-temperature applications.

P275N steel has equivalent or similar grades in other international standards:

These equivalents indicate that P275N pressure vessels steel has comparable performance across different global standards.

Due to its balanced properties, P275N Material is widely used in:

• Boiler manufacturing
• Pressure vessels and tanks
• Oil & gas storage equipment
• Heat exchangers
• Power plant components

It is especially suitable for applications requiring good weldability, moderate strength, and stable performance under pressure.

The grade of P275N pressure vessel steel plate refers to a normalized fine-grained steel with a minimum yield strength of 275 MPa, produced according to EN 10028-3.

It is a reliable and cost-effective P275N pressure vessel steel widely used in industrial equipment and pressure systems.

If you are looking for a trusted P275N Steel Supplier, we provide high-quality P275N Material with full certification, competitive pricing, and fast delivery.

Contact us today to get the latest quotation and technical support for your project.

Contact now to get P275N steels Quote

What are the core differences between P275N, P275NH, P275NL1, and P275NL2?

The core differences lie in impact test temperature and applicable working conditions. All four grades have a minimum yield strength of ≥275MPa (for thickness ≤16mm) and comply with the EN 10028-3 standard:

P275N: Impact test at -20°C, suitable for normal-temperature pressure vessels and general industrial pipelines;

P275NH: Impact test at -20°C, optimized for high-temperature performance, adaptable to medium-to-high temperature pressure equipment below 350°C;

P275NL1: Impact test at -40°C, suitable for low-temperature storage tanks and separators in cold regions;

P275NL2: Impact test at -50°C, offering the best ultra-low temperature toughness, adaptable to cryogenic equipment such as liquid nitrogen/LNG systems.

What are the corresponding numerical designations for these four grades?

P275N: 1.0483;

P275NH: 1.0485;

P275NL1: 1.0488;

P275NL2: 1.1104.

Does thickness affect performance?

Yes, it does. When the thickness exceeds 16mm, the yield strength gradually decreases (e.g., ≥245MPa for 63~100mm), and the low-temperature toughness also slightly declines. For ultra-low temperature working conditions with thickness ＞40mm, it is recommended to prioritize P275NL2 and increase the sampling ratio for impact tests.

What are the key mechanical property indicators of the four grades?

Yield Strength (ReH): ≥275MPa for thickness ≤16mm, slightly decreasing with increasing thickness (e.g., ≥255MPa for 40~63mm);

Tensile Strength (Rm): 410~560MPa;

Impact Energy (KV): ≥27J for each corresponding impact temperature (regular supply meets ≥40J to enhance safety redundancy);

Elongation (A): ≥22%~24% (adjusted with thickness).

What is the range of available dimensions?

Thickness: 6mm~300mm;

Width: 1500mm~4800mm;

Length: 6000mm~18000mm;

Customized cutting, drilling, and beveling services are available, with a minimum cutting size of 500×500mm.

How is the weldability, and what are the welding recommendations?

It has excellent weldability (CEV ≤0.43%), with recommended solutions:

Welding Consumables: E5515-C1 for manual arc welding, H08MnA+F55A4 flux for submerged arc welding, and ER50-6 for gas metal arc welding;

Preheating Requirement: No preheating required for thickness ≤30mm; preheat to 100~150°C for thickness ＞30mm;

Interpass Temperature: ≤250°C, with heat input controlled at 15~35kJ/cm;

Post-Weld Heat Treatment (PWHT): Recommended for thick plates (＞50mm) – stress relief annealing at 580~620°C for 2 hours.

Can the P275 series be substituted for ASTM A516 Gr70 (American standard) or Q345R (Chinese standard)?

vs. ASTM A516 Gr70: Similar strength, but the P275 series offers better low-temperature toughness . The P275 series is preferred for European projects, while ASTM A516 Gr70 is suitable for North American projects;

vs. Q345R (GB 713): Q345R has higher yield strength (≥345MPa), but the P275 series excels in low-temperature performance (-20°C impact) and high-temperature stability. For international projects, it is recommended to select according to the EN standard first.

What are the differences between P275NL1/NL2 and 16MnDR (Chinese standard)?

16MnDR (GB 3531): Impact test at -40°C, yield strength ≥315MPa, suitable for domestic low-temperature projects;

P275NL1: Impact test at -40°C, yield strength ≥275MPa, belonging to the European standard system with higher international recognition;

P275NL2: Impact test at -50°C, offering better low-temperature toughness than 16MnDR, adaptable to more severe cryogenic working conditions.