Q345R Steel Plates Of Pressure Vessel
Q345R steel Product Introduction
When yield ratio is ≤ 0.75, more than 0.8 might have higher risk of crack forming. Preheating of steel plate welding is not required. When steel plate thickness is ≤34, preheat to 100 ~ 150 ℃ when steel plate thickness is > 34, additionally eliminate stress is needed after welding heat treatment, heating temperature range 600 ~ 640 ℃, usually air cooling after the heat preservation furnace cooling to under 400 ℃.
When the carbon content of partial minimum Q345R steel welding basic no strict limits on line, for it is overheating sensitivity is not high, cold cracking tendency is low, but for the goodness of plasticity and toughness overheated zone, small linear energy is better.
When welding Q345R steel of carbon content on the high side, for the hardening tendency increases, the content of martensite increases, it will cause the string cable energy cold cracking tendency increase, embrittlement of overheated zone also become serious, this situation is offline energy partial bigger is better.
Q345R Steel plate Product Details
Main chemical elements composition
| C | Si | Mn | P | S | Alt(min.) |
| ≤0.20 | ≤0.55 | 1.20-1.60 | ≤0.025 | ≤0.015 | ≥0.020 |
steel plate Product Image
GNEE Group Team Photo
Committed to strict quality control and dedicated customer service, we have an experienced production staff ready to meet your needs and ensure customer satisfaction. We guarantee you a pleasant stay in China.
GNEE Group Exhibition Pictures
GNEE Group customers visit
If you have more needs and questions about Q345R steel, we are happy to advise you!
Hot Tags: q345r steel plates of boiler and pressure vessel steel, China q345r steel plates of boiler and pressure vessel steel manufacturers, suppliers, factory, Hardox steel, Niobium Alloy bar, Inconel 625 UNS N06625 Bars, Corten A, Q390 Angle Carbon Steel, low alloy steel plate